The structure of tetranatrolite from Mont Saint-Hilaire, Quebec (U.S. National Museum sample R1830) with a = 13.197(7) A, c = 6.630(9) A, and space group I42d, was refined using single-crystal X-ray data. A representative formula of tetranatrolite determined from electron microprobe analysis is Na12.50K0.01Ca2.93Sr0.11Al19.09 Si20.91O79.74??nH2O. The structure has the basic natrolite Si-Al-O framework configuration with Na, Ca, Sr, and K residing within inter-framework cages. Aluminum is disordered over the T1 and T2 tetrahedral sites, with T2 > T1. Water molecules O4 and O5 coordinate the intercage atoms and have high displacement parameters, indicating disorder within the cages. The Mont Saint-Hilaire tetranatrolite structure is compared to four previously determined structures, two tetranatrolite samples from Khibiny and Lovozero, Russia and two "gonnardite" samples from Tvedalen, Norway and Gignat, France. Observations are given to indicate that the Norwegian sample deduced to be tetranatrolite rather than gonnardite. Although the crystal structures of tetranatrolite and gonnardite are very similar, it is shown that the tetranatrolite compositions differ significantly from those of gonnardite. The tetranatrolite composition series varies along the join Na16Al16Si24O80-Na12 Ca4Al20Si20O80, and is represented by the formula Na16-xCaxAl16+xSi24-x O80??nH2O, where x extends from approximately 2.4 to 3.9. In contrast, gonnardites from Arkansas and Austria have compositions that vary along the join Na16Al16Si24O80-Na4 Ca8Al20Si20O80, which are represented by the formula ???xNa16-3xCa2xAl16+x Si24-xO80??nH2O and where ??? indicates vacant intercage cation sites and x varies from approximately 0.3 to 3.2. Tetranatrolite is a dehydration product of paranatrolite and probably does not have a true stability field.