Plasticity at crack tips in Gd3Ga5O12 garnet single crystals deformed at temperatures below 950°C
Links
- More information: Publisher Index Page (via DOI)
- Download citation as: RIS | Dublin Core
Abstract
Single crystals of Gd3Ga5O12 have been strained under confining pressure (1 5 GPa) at temperatures below 950°C. No evidence for macroscopic plasticity was found, but transmission electron microscopy revealed dislocation generation at crack tips. Deformation mechanisms are different from those operating in the high-temperature regime: extending stacking faults in {110} planes and the 〈010〉{100} glide system were observed. Dissociations of a/4〈111〉 partial dislocations were also observed.
Publication type | Article |
---|---|
Publication Subtype | Journal Article |
Title | Plasticity at crack tips in Gd3Ga5O12 garnet single crystals deformed at temperatures below 950°C |
Series title | Philosophical Magazine A: Physics of Condensed Matter, Structure, Defects and Mechanical Properties |
DOI | 10.1080/01418618508237568 |
Volume | 51 |
Year Published | 1985 |
Language | English |
Publisher | Taylor& Francis Online |
Contributing office(s) | Earthquake Science Center |
Description | 12 p. |
First page | 485 |
Last page | 496 |
Google Analytic Metrics | Metrics page |